Overview

LeesonGrip 3-1 PU4490/20 is a three-component solvent-free urethane system which when used with, for example, 1-3mm aggregate gives a High Friction Anti-Skid surface. Urethanes cure rapidly especially at low temperatures allowing earlier opening of sites to traffic. This is a significant advantage when application is made at night when temperatures are low.

Applications

  • Cycle Paths
  • Pedestrian Areas
  • Walkways
  • Drives
  • Pathways

See all applications in our Technical Data Sheet

See all applications in our Technical Data Sheet

How to use

  • Surface Preparation – Bituminous Surfaces

    The road surface should have a texture depth of between 0.5mm and 2.0 mm as determined by the sand patch test. All imperfections in the road surface should be repaired prior to laying the product.
    The surface to be treated must be clean, free from frost, ice, and road salt. The surface should also be sound, dry, and free from dust and any loose material. Any visible oil should be removed with a detergent solution, flushed with water and the surface allowed to dry.
    We also have available a cementitious scratch coat system (D5126), for filling porous asphalt to reduce topcoat consumption.

  • Surface Preparation - Concrete and timber

    Concrete is to be hot compressed air blasted then primed with primer PU3922 and this allowed to cure for a minimum of 2 hours and maximum of 12 hours before applying the finish coating. On timber, the surface should be primed with primer PU3922 and conditioned as above.

  • Surface Preparation - Steel

    It is to be shot blasted to SA2.½ and primed and allowed to cure 1-2 hours minimum, maximum 12 hours before finish coating.

  • Mixing and Application

    Mix A component well before addition of B and C component. Add 1 part by weight of LeesonGrip PU4490/20 Part B (curing agent) to 2.38 part by weight of LeesonGrip PU4490/20 Part A (resin) and mix until a mass of uniform colour is obtained. Add sand mix and mix until uniform. The surface is then coated with the blend within 10 minutes (@ 20°C) at a coverage rate of 2.5 kg per m (dependant on surface porosity). The resin should then be allowed to self-level to give total coverage. The non-slip aggregate (moisture content less than 0.4%) is then scattered over the resin within 5 minutes (@ 20°C) excess aggregate can be removed after 2 hours or when the resin has cured sufficiently. The site can be reopened to traffic after 4 hours, depending on ambient temperature, or when the binder is hard to the touch.
    DO NOT USE IN TEMPERATURES BELOW 5°C

Downloads

FAQs

What is the estimated coverage rate of PU4490/20?

Estimated coverage rate is approximately 2.5 kg/m² (dependant on surface porosity)

How soon after installed can the surface be reopened to traffic?

The site can be reopened to traffic after 4 hours depending on ambient temperature or until the binder is hard to the touch.